minus-squareNoah@fosscad.ioOPMBlinkfedilinkEnglisharrow-up1·29 days agou/bl1ndside · 2025-06-30 22:14:34 UTC · score 3 Yeah it’s great. I’d go with polymaker. If your printer is super solid, try Pa6-CF or pa12-cf
minus-squareNoah@fosscad.ioOPMBlinkfedilinkEnglisharrow-up1·29 days agou/Apprehensive-Mix3174 · 2025-06-30 22:18:27 UTC · score 2 My he dries it at a high temperature I heard I would like to try I have the machine for
minus-squareNoah@fosscad.ioOPMBlinkfedilinkEnglisharrow-up1·29 days agou/bl1ndside · 2025-06-30 22:20:30 UTC · score 1 What?
minus-squareNoah@fosscad.ioOPMBlinkfedilinkEnglisharrow-up1·29 days agou/Apprehensive-Mix3174 · 2025-06-30 22:21:13 UTC · score 1 Before you can print, do you have to dry it?
minus-squareNoah@fosscad.ioOPMBlinkfedilinkEnglisharrow-up1·29 days agou/bl1ndside · 2025-06-30 22:27:26 UTC · score 3 NylonCF, yeah you do. PLA pro should be fine without it. I have Bambu AMS HT and dry my nylon at 85C for a couple of days.
u/bl1ndside · 2025-06-30 22:14:34 UTC · score 3
Yeah it’s great. I’d go with polymaker. If your printer is super solid, try Pa6-CF or pa12-cf
u/Apprehensive-Mix3174 · 2025-06-30 22:18:27 UTC · score 2
My he dries it at a high temperature I heard I would like to try I have the machine for
u/bl1ndside · 2025-06-30 22:20:30 UTC · score 1
What?
u/Apprehensive-Mix3174 · 2025-06-30 22:21:13 UTC · score 1
Before you can print, do you have to dry it?
u/bl1ndside · 2025-06-30 22:27:26 UTC · score 3
NylonCF, yeah you do. PLA pro should be fine without it.
I have Bambu AMS HT and dry my nylon at 85C for a couple of days.