PPA-CF vs PA6-CF?
Does anyone have experience printing PPA-CF and PA6-CF? I had read that “PPA-CF is 48% stronger” than PA6 if you get good layer adhesion, but I’m seeing conflicting info regarding impact resistance. Anyone have input who’s printed and used both?
If you’re annealing at the correct temperature, there’s no need to pack PPA-CF in salt. The annealing temperature is well below the un-annealed heat deflection temperature so you shouldn’t experience any warping or distortion.